Al 1050 at a load of 5 kg | |||
Sample Variant | Depth of indentation (µm) | Depth after removal (µm) | Vicker Hardness (N/mm2) |
Duplex nickel + Hexavalent chromium | 42 | 32 | 5255.102 |
Duplex nickel + Hexavalent chromium + electroless nickel undercoat | 55 | 52 | 3064.463 |
Duplex nickel + Trivalent chromium | 52.5 | 40 | 3363.265 |
Duplex nickel + Trivalent chromium + electroless nickel undercoat | 58 | 46 | 2755.648 |
Sample Variant | Al 6061 at a load of 5 kg | Vicker Hardness (N/mm2) | |
Duplex nickel + Hexavalent chromium | 38 | 32 | 6419.668 |
Duplex nickel + Hexavalent chromium + electroless nickel undercoat | 48 | 36 | 4023.438 |
Duplex nickel + Trivalent chromium | 39 | 33 | 6094.675 |
Duplex nickel + Trivalent chroium + electroless nickel undercoat | 58 | 52 | 2755.648 |